Basalt Chopped Fibers can be mixed directly into polymers and concrete to increase tensile strength, reduce cracking and chipping. 

Perfect for mortar and concrete reinforcement applications; all decorative applications as countertops, fireplace surrounds. 

• Diameter is 17 microns.  Fiber lengths are available in 12 mm, 18 mm and 24 mm / .47", .70", .94" 

• Fibers are completely resistant to the effects of the alkali in concrete, and require no special coatings for concrete use 

• Fibers resist cold down to -260 degrees F, and heat up to 1,500 degrees F

• Fibers do not conduct electricity or induce electrical fields 

• Fibers do not absorb or wick water into reinforced structures 

• Fibers significantly improves the shock resistance of concrete 

• Ductility index of basalt fiber reinforced concrete increases by a factor of 2~4. 

• The addition of basalt fiber can effectively increase the compressive strength, splitting the tensile and flexural strength (especially splitting tensile and flexural strength) of the concrete; values of 9.9%, 37.5% and 44.2% are attained 

• Crack impact cycle number of the concrete improves by 60%~ 170%, the impact energy improves by 90%~ 260%, and the ductility index increases by a minimum of two times, compared with ordinary concrete 

Basalt Fibers advantages:

 - Stronger than fiberglass in tensile strength 

- Non-respirable, inert and safe to work with 

- 27% better elastic modulus 

- UV immune 

- Non-conductive 

- Will not harbor bacterial or microbial growth 

- Better impact resistance, does not shatter like carbon fibers 

- Ten times better electrical insulator than fiberglass

- Very resistant to aggressive liquids, acids and alkalies - Great sound attenuation properties 

- Replacement for asbestos in frictional material applications 

- Over twice the strength retention in elevated temperatures than E-glass reinforced applications; better and more stable frictional coefficient and longer life 

- Higher sound insulation properties than e-glass fibers

- Lower heat transfer coefficient than e-glass and carbon with greater thermal insulation properties 

- Low coefficient of thermal expansion; approximately the same as concrete 

Basalt Fiber has a similar chemical composition as regular glass fiber but Basalt Fiber has better strength characteristics, and unlike most glass fibers is highly resistant to acidic and salt attack and alkaline, making it a good option for concrete, bridge and shoreline structures.

Compared to carbon and aramid fiber, Basalt Fiber has the features of wider application temperature range -452° F to 1,200° F (-269° C to +650° C), higher compression strength and higher shear strength, radiation resistance and higher oxidation resistance

Basalt fiber dosage

Regular concrete mix

We recommend 6-8 pounds of basalt chopped fibers per cubic yard of concrete.

GFRC concrete mix

Fiber content varies but is generally approximately 3% to 7% of the cementitious material weight or 1% to 3% by total concrete weight. Increased fiber content adds strength but decreases workability.

Common water to cement ratios used from 0.25 to 0.35. (25-35% by cementitious material weight)